TOP > 外国特許検索 > Intermetallic compound superconductors and alloy superconductors, and method for their preparation

Intermetallic compound superconductors and alloy superconductors, and method for their preparation 実績あり

外国特許コード F110005110
整理番号 A061-16US
掲載日 2011年8月23日
出願国 アメリカ合衆国
出願番号 22027202
公報番号 20030017949
公報番号 6956011
出願日 平成13年7月24日(2001.7.24)
公報発行日 平成15年1月23日(2003.1.23)
公報発行日 平成17年10月18日(2005.10.18)
国際出願番号 JP2001006383
国際公開番号 WO2002055435
国際出願日 平成13年7月24日(2001.7.24)
国際公開日 平成14年7月18日(2002.7.18)
優先権データ
  • 特願2001-001948 (2001.1.9) JP
  • 2001WO-JP06383 (2001.7.24) WO
発明の名称 (英語) Intermetallic compound superconductors and alloy superconductors, and method for their preparation 実績あり
発明の概要(英語) (US6956011)
There are provided an intermetallic compound superconductor that is high in superconducting transition temperature, and an alloy superconductor that is high in superconducting transition temperature and excels in malleability and ductility, as well as a method of making such a superconductor with good reproducibility and at a low cost of manufacture.
This entirely new intermetallic compound superconductor is made of magnesium (Mg) and boron (B) and has a chemical composition expressed by formula: Mg1B2, has a hexagonal AlB2 type crystallographic structure and has a superconducting transition temperature (Tc) of 39 K.
An alloy containing this intermetallic compound excels in malleability and ductility and constitutes the alloy superconductor having a superconducting transition temperature (Tc) of 39 K.
In the method of manufacture, a Mg containing feedstock powder and a B containing feedstock powder are mixed together to form a mixture thereof which is, e.g., hot pressed to produce a semiconductor product.
特許請求の範囲(英語) [claim1]
1. A method of conducting electrical current, comprising the steps of: providing an intermetallic compound superconductor of a composition expressed by chemical composition formula: Mg1B2 and having a hexagonal AlB2 type crystallographic structure in which a Mg layer and a B layer lie alternately;
and bringing said compound superconductor to a temperature of 39 K or lower, and passing electrical current through said compound superconductor.
[claim2]
2. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of: mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2, shaping said mixture powder into the form of a pellet, and heating said pellet in an inert gas to form the intermetallic compound superconductor;
bringing said intermetallic compound superconductor to a temperature of 39 K or lower;
and passing electrical current through said intermetallic compound superconductor.
[claim3]
3. A method of conducting electrical current as set forth in claim 2, wherein said heating step is conducted at a temperature of 700 to 2000 deg. C. for a period of several seconds or more.
[claim4]
4. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of: mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2, shaping said mixture powder into the form of a pellet, and heating said pellet in a vacuum to form the intermetallic compound superconductor;
bringing said intermetallic compound superconductor to a temperature of 39 K or lower;
and passing electrical current through said intermetallic compound superconductor.
[claim5]
5. A method of conducting electrical current as set forth in claim 4, wherein said heating step is conducted under a pressure of 2 * 10-2 Pa or less at a temperature of 650 to 1100 deg. C. for a period of several minutes or more.
[claim6]
6. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of: mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2, shaping said mixture powder into the form of a pellet, and heating said pellet in a pressurized inert gas to form the intermetallic compound superconductor;
bringing said intermetallic compound superconductor to a temperature of 39 K or lower;
and passing electrical current through said intermetallic compound superconductor.
[claim7]
7. A method of conducting electrical current as set forth in claim 6, wherein said heating step is conducted under a pressure of 1 to 200 MPa at a temperature of 600 to 1100 deg. C. for a period of several minutes or more.
[claim8]
8. A method of conducting electrical current, comprising the steps of: forming an intermetallic compound superconductor by the steps of: mixing a Mg containing feedstock powder and a B containing feedstock powder together to form a mixture powder thereof so that the mixture powder contains Mg and B at a compositional ratio of Mg/B=1/2, shaping said mixture powder into the form of a pellet, and pressing and heating said pellet to form the intermetallic compound superconductor;
bringing said intermetallic compound superconductor to a temperature of 39 K or lower, and passing electrical current through said intermetallic compound superconductor.
[claim9]
9. A method of conducting electrical current as set forth in claim 8, wherein said pressing and heating step is conducted under a pressure of 0.1 to 6 GPa at a temperature of 700 to 1400 deg. C. for a period of several minutes or more.
  • 発明者/出願人(英語)
  • AKIMITSU JUN
  • ZENITANI YUJI
  • MURANAKA TAKAHIRO
  • NAKAGAWA NORIMASA
  • NAGAMATSU JUN
  • JAPAN SCIENCE AND TECHNOLOGY AGENCY
国際特許分類(IPC)
参考情報 (研究プロジェクト等) CREST Phenomena of Extreme Conditions AREA
ライセンスをご希望の方、特許の内容に興味を持たれた方は、問合せボタンを押してください。

PAGE TOP

close
close
close
close
close
close