Top > Search of International Patents > GOLD COMPOSITE MATERIAL, METHOD FOR MANUFACTURING SAME, AND GOLD NANOCATALYST

GOLD COMPOSITE MATERIAL, METHOD FOR MANUFACTURING SAME, AND GOLD NANOCATALYST

Foreign code F170009242
File No. (S2016-0544-N0)
Posted date Sep 21, 2017
Country WIPO
International application number 2017JP009072
International publication number WO 2017154927
Date of international filing Mar 7, 2017
Date of international publication Sep 14, 2017
Priority data
  • P2016-046360 (Mar 9, 2016) JP
  • P2016-121460 (Jun 20, 2016) JP
Title GOLD COMPOSITE MATERIAL, METHOD FOR MANUFACTURING SAME, AND GOLD NANOCATALYST
Abstract [Problem] To provide a novel gold composite material having higher catalytic activity than conventional gold nanoparticle catalysts, a method for manufacturing the gold composite material, and a gold nanocatalyst in which the gold composite material is used.
[Solution] A gold composite material comprising a carrier and gold microparticles carried on the carrier, the gold composite material being characterized in that the carrier is an acidic solid metal oxide. A method for manufacturing a gold composite material, wherein the method for manufacturing a gold composite material is characterized in being provided with a carrying step for carrying gold microparticles using the acidic solid metal oxide and a gold colloid solution, and in the carrying step, a solid metal oxide having a high specific surface area of at least 20 m2/g is used as the solid metal oxide, and a gold colloid solution containing gold particles having a particle diameter of 5 nm or less is used as the gold colloid solution.
Outline of related art and contending technology BACKGROUND ART
Gold nanoparticles supported on the support as is known to show high catalytic ability and, various gold nanoparticle catalyst have been proposed.
Patent Document 1 is for example, of gold nanoparticles as the support for the non-noble metal oxide, noble metal oxide is MoO3 CuO and one or more selected from the group consisting of whether the 1, 1 or composite oxide containing two or more them by selecting, in the gaseous phase and acetaldehyde from ethanol can be selectively produced, gold nano-catalyst has been proposed.
In addition, Patent Document 2 is, as a catalyst used in the preparation of the pyridine compound, the surface of the carrier surface immobilized gold nanoparticles immobilized gold and use of a catalyst, the surface immobilized gold as a catalyst, hydroxyapatite (HAP), titania (TiO2) 、alumina (Al2 O3) 、magnesia (MgO), silica (SiO2) 、ceria (CeO2) 、such as activated carbon is used as a carrier (C) is disclosed.
Scope of claims (In Japanese)[請求項1]
担体と該担体上に担持された金微粒子とからなる金複合材料であって、
上記担体が、酸性の固体金属酸化物であることを特徴とする金複合材料
[請求項2]
上記固体金属酸化物が、
酸化ニオブ、ポリオキソメタレート、酸化タングステン、酸化タンタル、酸化モリブデン、酸化バナジウムからなる群より選択される一種以上であることを特徴とする請求項1記載の金複合材料。
[請求項3]
担持されている上記金微粒子の粒径が、5nm以下であることを特徴とする請求項1記載の金複合材料。
[請求項4]
上記固体金属酸化物の比表面積が20m2/g以上であることを特徴とする請求項1記載の金複合材料。
[請求項5]
上記担体上に担持された上記金微粒子の密度が2μmol・m-2以下であることを特徴とする請求項4記載の金複合材料。
[請求項6]
上記固体金属酸化物は、該固体金属酸化物を構成する結晶格子により形成された結晶構造体であり、一つの結晶格子により形成されるか又は複数の結晶格子が集合して形成される格子点と該格子点の周囲に形成される空隙とを有し、該空隙は各格子点又は該結晶格子と同様の大きさを有する通常空隙と、各格子点よりも大きい大空隙とを有する
ことを特徴とする請求項1記載の金複合材料。
[請求項7]
上記大空隙の容量(メソ孔容量)が0.1cm3/g以上である
ことを特徴とする請求項6記載の金複合材料。
[請求項8]
請求項1~7のいずれかに記載の金複合材料からなり、
バイオマス由来の成分の酸化に用いられる
金ナノ触媒。
[請求項9]
請求項1記載の金複合材料の製造方法であって、
酸性の固体金属酸化物と金コロイド溶液とを用いて金微粒子の担持を行う担持工程を具備し、
上記担持工程においては、
上記固体金属酸化物として、比表面積が20m2/g以上の高比表面積のものを用い、
上記金コロイド溶液として、粒径5nm以下の金粒子を含有する金コロイド溶液を用いることを特徴とする金複合材料の製造方法。
[請求項10]
請求項1記載の金複合材料からなる、有機化合物の酸化反応用の金ナノ触媒。
  • Applicant
  • ※All designated countries except for US in the data before July 2012
  • TOKYO METROPOLITAN UNIVERSITY
  • Inventor
  • HARUTA Masatake
  • MURAYAMA Toru
  • YOSHIDA Takuya
IPC(International Patent Classification)